Abstract

The validity of fracture toughness data obtained from tests with V-notched bending bars is affected by the notch root radius and the presence of R-curve behavior. A macroscopic test specimen has been developed that contains a notch introduced by focused ion beam machining. This produces a notch root radius of less than 0.1 mu m, so that notch effects can be ignored for most ceramics. Also, due to the very small notch depths the influence of a rising R-curve should be very close to that of natural cracks. First tests, carried out on a Ce-doped zirconia ceramic resulted in a toughness of K (Ic) a parts per thousand 5.9 MPaasm.