Vacancy-like defects in doped PbZr60Ti40O-3 observed by positron lifetime and coincident Doppler spectroscopy

  • Autor:

    Puff, W; Kungl, H; Hoffmann, MJ; Gottschalk, S; Balogh, AG

  • Quelle:

    POSITRON ANNIHILATION, ICPA-13, PROCEEDINGS 445-4 (2004), 171–173 

  • Vacancy-like defects in doped Pb(Zr60Ti40)O-3 observed by positron lifetime and coincident Doppler spectroscopy.


Ferroelectric Pb(Zr60Ti40)O-3 ceramics sintered for 6 hours at 1050 degreesC in air and doped with La or Nb in the range 0.5 to 6 mol% have been investigated by positron lifetime spectroscopy and two-dimensional coincident Doppler measurements. The undoped samples show two lifetime components with a defect lifetime of about 250 ps. After doping this defect lifetime increases to about 295 ps. The influence of the doping on the Doppler spectra is extremely small. Additional XRD pattern show a significant correlation between doping and lattice structure.